Haynes 25™ - UNS R30605 Alloy L605
Haynes 25™ has an excellent temperature strength and oxidation resistance to 2000 °F. Haynes 25™ is hot formable between 1900 ≥F- 2300 °F. Also known as Alloy L605, it is better to cold-work Haynes 25™ for bending, spinning and drawing the components.
Available forms are seamless pipe, welded pipe, seamless tube, welded tube, bar, wire, sheet, plate, forgings, pipe fittings and flanges.
 |
|
|---|---|
Sheet/Plate content |
AMS 5537 |
Round Bar/Wire content |
AMS 5759 |
Weld Wire | AMS 5796 |
 | |
|---|---|
C (Carbon content) |
.05 - .15 |
| MN | 1.0 - 2.0 |
| P | .4 |
| S | .03 |
Si |
.4 |
Cr |
19.0 -21.0 |
Ni |
9.0 - 11.0 |
Mo | |
Cu | |
Co |
bal |
| Cb | |
Ti (Titanium contenet) |
|
Al (Aluminum content) |
|
Fe (Iron content) |
3.0 |
| W | 14.0 -16.0 |